There are various Stainless Steel Welded Tube and Seamless Tube for the Food Industry.

Specification Comparison

· AS 1528.1 “Specification for tubes (stainless steel) for the food industry”
· ASTM A249 “Specification for welded austenitic steel boiler, superheater, heat exchanger, and condenser tubes”
· ASTM A269 “Specification for seamless & welded austenitic stainless steel tubing for general service”
· ASTM A270 “Specification for seamless & welded austenitic stainless steel sanitary tubing”
· ASTM A554 “Specification for welded stainless steel mechanical tubing”
AS1528 was revised in 2001 (after many years of disuse), by key stake-holders in the Australian tube industry and food manufacturing industries. AS 1528 is unique in that it covers all the associated fittings, in addition to the tube.

Material
All specifications call for the common grades 304, 304L, 316 and 316L. Most specifications allow a number of other stainless steel grades as well. AS1528.1 permits all grades of austenitic and duplex stainless steel listed in ASTM A240, so the possibilities are very extensive.

Manufacture
All specifications require fusion welded tube without filler metal (in practice this permits standard tube production using TIG or plasma welding). AS 1528, A269 and A270 also cover seamless product, if requested, although this is rarely required.

Dimensional Tolerances
Wall Thickness
· A249 requires ±10% of nominal - no nominal thicknesses are stipulated.
· A269 requires ±10% of nominal for sizes over ?" - no nominal thicknesses are stipulated.
· A270 requires ±12.5% of nominal - no nominal thicknesses are stipulated.
· A554 requires ±10% of nominal - no nominal thicknesses are stipulated.
· AS 1528 specifies nominal thicknesses of 1.6mm for all ODs except 2.0mm for 203.2mm OD; other thicknesses can be specified by purchasers. Standard tolerance is +nil, -0.10mm. The all-minus tolerance recognises the usual practice for tube, to all specifications, to be produced towards the lower limit of the tolerance range. A range of between 1.52 and 1.58mm is typical. This tolerance also applies to tube fittings.

Surface Finish
· A249 and A269 both require surfaces “free of scale” – annealing of the tube is normally done in a controlled atmosphere and this “bright annealed” finish is considered acceptable.
· A270 requires selection of both internal and external surfaces. The possible conditions range from a "mill finish" (i.e. the strip's 2B finish, without any subsequent polishing), to abrasive polishing with 80, 120, 180 or 240 grit, to special polishing and electropolishing. Surface finishes may also be specified in terms of Ra values, but no limits are given in the specification.
· A554 requires only "free of scale" and implies a "direct off mill" finish as standard. Clause 11.2 does allow - "If special finishes are required, they shall be stated in the order". Thus a large proportion of A554 tube used in the Australian market is supplied in the externally polished or buffed conditions, in the range of about 180 - 320#, or with a very highly polished surface, typically stated as 600#.
· AS1528 specifies the external surface "as produced" or "buff polished", as agreed. The internal surface is required to be 2B finish, quoted as typically 0.3μm Ra. Work done by Atlas Steels indicates that for 1.6mm 2B coil (the starting material for welded tube) the typical roughness is 0.10 - 0.20 μm Ra; this would be expected to not be significantly degraded in the manufacture of tube. With weld bead rolling it would be expected that the finish of the weld would be similar to that of the parent tube.

Weld Bead
The food industry generally requires a tube with no weld bead remnant on the inside surface if the intended service is handling product.
· A249 requires that at least the weld be cold worked after welding and before final heat treatment.
· A269 does not require any weld bead control or cold working.
· A270 makes no mention of weld bead.
· A554 can be supplied with the weld bead left on, but in recent years Australasian manufacturers of As Welded tube have all made internal weld bead rolling a fairly routine procedure; this therefore complies with the "Bead Removed" option of A554. (Weld bead rolling is not generally possible in sizes below 31.8mm, although sizes down to 25.4 or even smaller can be hammer swaged if specifically ordered).
· AS1528 requires removal of the weld bead (except in the small sizes where the procedure is not possible). There is also a requirement that the internal surface be smooth, with no lack of weld penetration and no crevices adjacent to welds. This requirement addresses the heart of the issue - freedom from sites for product or bacterial build-up.

Heat Treatment
· A249, A269 and A270 all require that “all material shall be furnished in the heat treated condition”. Heat treatment is annealing (also referred to as solution treatment or solution annealing). In practice this is not a common requirement for food industry tube unless it requires significant bending or flaring.
· A554 is normally supplied “as welded”, ie. no heat treatment after tube forming (although the tube will be produced from strip which has itself been annealed just prior to the final cold roll). There is the possibility of calling for A554 tube in the annealed condition, but this is never done - annealed tube (“As Welded Annealed” or AWA) is more usually specified to ASTM A269.
· AS1528 allows either annealed or un-annealed conditions to be specified by the purchaser.

Mechanical Properties
· A249 is intended for critical environments in boilers or heat exchangers, and hence extensive mechanical testing is required. Full tensile and hardness testing is standard, as are flattening, flange and reverse bend.
· A269 requires no tensile testing, but does require hardness tests, plus flange, reverse flattening.
· A270 requires a reverse flattening test only.
· A554 requires no mechanical testing as standard.
· AS1528 requires no tensile or hardness testing, but does require the tube to be made from strip compliant with ASTM A240 - which itself has tensile strength requirements.

Non-Destructive Inspection
· A249, A269, A270 and AS1528.1 all require 100% hydrostatic or eddy current testing.
· A554 includes the possibility of non-destructive testing as a supplementary requirement, but this is not usual for A554 tube.